NaAlO2改性ZSM-5分子筛的制备及其在甲醇芳构化中的应用

石油炼制与化工 ›› 2016, Vol. 47 ›› Issue (2): 47-52.

NaAlO2改性ZSM-5分子筛的制备及其在甲醇芳构化中的应用

夏腾飞¹,魏振浩¹,曹庆胜¹,朱学栋^1,2

1. 华东理工大学化工学院大型工业反应器工程教育部工程研究中心

2. 华东理工大学化学工程联合国家重点实验室

收稿日期:2015-07-06 修回日期:2015-09-15 出版日期:2016-02-12 发布日期:2016-01-29
通讯作者: 朱学栋 E-mail:xdzhu@ecust.edu.cn

METHANOL AROMATIZATION PERFORMANCE OF ZSM-5 MODIFIED BY NaAlO2

Received:2015-07-06 Revised:2015-09-15 Online:2016-02-12 Published:2016-01-29

摘要/Abstract

摘要：

采用NaAlO2和HCl两步法对ZSM-5分子筛进行改性，运用XRD、SEM、NH3-TPD、N2吸附-脱附、ICP-OES、TG等方法对改性前后的分子筛进行表征。结果表明:经NaAlO2改性后的ZSM-5分子筛中引入了介孔，且分子筛的晶型、酸性、微孔体积等保持较好，并具有较高的固相收率；酸洗前通过中间焙烧有利于消除孔道覆盖和恢复酸性。将改性后的分子筛应用于甲醇芳构化反应中，在温度400 ℃、压力0.15 MPa、质量空速1.9 h-1的反应条件下，经0.45 mol/L NaAlO2改性的分子筛反应效果最优，产物芳烃收率可达41.9%，BTX收率达32.7%；与原粉分子筛相比，产物芳烃收率提高了3.8百分点，BTX收率提高了4.4百分点；同时，其反应稳定性可达30 h，较原粉延长了1倍多。

关键词: ZSM-5, NaAlO2, 介孔, 甲醇, 芳构化

Abstract:

ZSM-5 zeolite was modified successively by sodium aluminate and HCl washing with a calcination between the two steps. The samples were characterized by XRD, SEM, NH3-TPD, N2 adsorption, ICP-OES, and TG techniques. The results show that mesopores were created, and a higher solid yield was obtained with the crystallinity, acidity and micropore volume largely preserved. Besides, the calcination before acid washing is in favor of eliminating the pore blocking and recovering the acidity. The methanol aromatization performance over the modified catalysts was investigated at the conditions of 400 ℃, 0.15 MPa and the weight hourly space velocity of 1.9 h-1. The ZSM-5 zeolite modified with 0.45 mol/L NaAlO2 presents the optimal performance. The aromatics yield reaches 41.9% and BTX yield is 32.7%, increased by 3.8 and 4.4 percentage points compared with catalytic activity of parent ZSM-5, respectively. Meanwhile, the modified catalyst’s lifetime is 30h, one more times than the parent zeolite.

Key words: ZSM-5, NaAlO2, mesoporous, methanol, aromatization

夏腾飞魏振浩曹庆胜朱学栋. NaAlO2改性ZSM-5分子筛的制备及其在甲醇芳构化中的应用[J]. 石油炼制与化工, 2016, 47(2): 47-52.

参考文献

[1] 邢爱华，孙琦.甲醇制芳烃催化剂开发进展[J].现代化工，2013,33(3)：29-32 [2] 孙富伟，劳国瑞，卢秀荣等.煤基甲醇芳构化技术的研究及应用进展[J].现代化工，2014,34(2)，27-32 [3] 张贵全，白婷，屈文婷等.甲醇芳构化的研究II.NaOH处理HZSM-5分子筛催化剂的性能[J].石油化工，2013,42(3):265-269 [4] Rosario Caicedo-Realpe, Javier Pérez-Ramírez. Mesoporous ZSM-5 zeolites prepared by a two-step route comprising sodium aluminate and acid treatments[J].Microporous and Mesoporous Materials,2010,128(1-3):91-100 [5] Aguayo AT, Mier D, Gayubo AG, et al.Kinetics of Methanol Transformation into Hydrocarbons on a HZSM-5 Zeolite Catalyst at High Temperature(400-550oC)[J].Industrial and Engineering Chemistry Research,2010,49(24):12371-12378 [6] Danny V, Sharon M, Maria M, et al. Full Compositional Flexibility in the Preparation of Mesoporous MFI Zeolites by Desilication[J]. The Journal of Physical Chemistry C,2011,115(29):14193-14203 [7] Danny V, Rosario C, Adriana B, et al. Properties and Functions of Hierarchical Ferrierite Zeolites Obtained by Sequential Post-Synthesis Treatments[J]. Materials Chemistry,2010,22(16):4679-4689 [8] Fernandez C, Stan I, Gilson JP, et al. Hierarchical ZSM-5 zeolites in shape-selective xylene isomerization: role of mesoporosity and acid site speciation[J]. Chem. Eur. J.,2010,16:6224-6233 [9] Martin S, Esben T, Kresten E, et al. Catalysis with hierarchical zeolites[J].Catalysis Today,2011,168(1):3-16 [10] Jeongnam Kim, Minkee Choi, Ryong Ryoo. Effect of mesoporosity against the deactivation of MFI zeolite catalyst during the methanol-to-hydrocarbon conversion process[J].Journal of Catalysis,2010,269(1):219-228 [11] Guisnet M, Costa L, Ribeiro F R. Prevention of zeolite deactivation by coking[J].Journal of Molecular Catalysis A: Chemical,2009,305(1-2):69-83

[1]	牛丛丛栾学斌徐润夏国富. 分布式甲醇重整制氢动力学及反应器强化研究[J]. 石油炼制与化工, 2024, 55(3): 67-74.
[2]	王佳静王建文李茂帅宋奕慧王石维吕静鲍晓军马新宾. CO₂催化加氢合成甲醇研究进展[J]. 石油炼制与化工, 2024, 55(2): 75-83.
[3]	陈自娇罗利平张博郭勤苗鹏杰. CO₂与甲醇直接合成碳酸二甲酯的催化剂研究进展[J]. 石油炼制与化工, 2024, 55(2): 84-90.
[4]	张雨管泽坤赵亭潘原柳云骐. Ni/ZnO-Zn/ZSM-5双功能耦合催化剂的制备及反应吸附脱硫耦合芳构化反应性能研究[J]. 石油炼制与化工, 2024, 55(2): 160-167.
[5]	刘红星丁佳佳申学峰王传明齐国祯王仰东谢在库. 从基础研究到工业转化应用的实践—甲醇制烯烃SMTO催化技术开发[J]. 石油炼制与化工, 2024, 55(1): 122-129.
[6]	夏长久杨焯林民朱斌彭欣欣汪燮卿舒兴田. 空心钛硅分子筛催化材料：从理性设计到工业应用[J]. 石油炼制与化工, 2024, 55(1): 18-27.
[7]	王晶刘生海齐欢高斌李东郭晓峰王旭张君兰. 甲醇制烯烃工业装置水洗水系统问题分析及解决方案[J]. 石油炼制与化工, 2023, 54(8): 37-42.
[8]	孙敏沈宁元黄志青欧阳颖宋海涛. 多级孔ZSM-5分子筛在增产丙烯助剂中的应用[J]. 石油炼制与化工, 2023, 54(8): 58-66.
[9]	李雪礼侯硕旻段宏昌路瑞玲张琰图. 磷改性工艺对ZSM-5分子筛催化裂化增产丙烯性能的影响[J]. 石油炼制与化工, 2023, 54(8): 74-82.
[10]	郭振莲牟庆平李新王文静王小燕董松祥王兴之. CdS/CeO₂异质结纳米光催化剂催化还原CO₂的研究[J]. 石油炼制与化工, 2023, 54(6): 46-54.
[11]	沈宇李明丰朱强强褚阳. 多级孔分子筛制备方法研究进展[J]. 石油炼制与化工, 2023, 54(2): 108-116.
[12]	赵新来周广林吴谦郭修程. ZSM-5催化异丁烯胺化制叔丁胺的研究进展[J]. 石油炼制与化工, 2023, 54(2): 126-133.
[13]	鲁景山方亚平迪丽努尔·艾力苗聪慧廖正坤艾沙·努拉洪. 以高岭土为铝源合成ZSM-5分子筛及其CO₂吸附性能研究[J]. 石油炼制与化工, 2023, 54(2): 90-99.
[14]	徐润栾学斌夏国富宋烨林伟. 模块化分布式甲醇制氢系统开发和站内制氢实践[J]. 石油炼制与化工, 2023, 54(11): 1-7.
[15]	陈永浩董晨王杰广王子健. 正丁烷芳构化九集总反应动力学模型研究[J]. 石油炼制与化工, 2023, 54(11): 96-100.