STUDY ON LOW TEMPERATURE PYROLYSIS OF WASTE TIRE TO PRODUCE OIL

Received:2018-07-18 Revised:2018-08-22 Online:2019-02-12 Published:2019-02-25
Supported by:

摘要/Abstract

摘要： 为了解废轮胎橡胶充分资源化处理规律，进行了轮胎胶粒低温热解研究，开展了铝甑干馏实验、热重试验等。结果表明：废轮胎低温热解处理以产热解油为主，其次是炭黑产物；其中，热解油收率为52.7%，炭黑为38.0%；热解瓦斯气满足热解工艺的热能需求，无需外部燃料；500 ℃可实现轮胎充分热解，但耗时较长，约180 min，因此在设备研发过程中需考虑改进热解工艺，提高设备效率。

关键词: 废轮胎, 热解油, 炭黑

Abstract: The low-temperature pyrolysis of the scrap tire was investigated by Fisher assay test and thermogravimetric test. Results showed that the main products were pyrolysis oil and carbon black with yield of 52.7% and 38.0%, respectively. The pyrolytic gas can meet the thermal energy demand of pyrolysis process without external fuel. The tire pyrolysis can be fully finished at 500℃, but takes longer time, about 180 min. Thus, it needs to improve pyrolysis process to enhance the equipment efficiency.

Key words: waste tire, pyrolysis oil, carbon black

中图分类号:

李成张斌林红邓少奎刘波. 废轮胎低温热解制油研究[J]. 石油炼制与化工, 2019, 50(2): 27-30.

[1]	刘明星章群丹刘泽龙李明丰. 废塑料热解油性质及组成的研究现状[J]. 石油炼制与化工, 2023, 54(4): 133-144.
[2]	刘明星王乃鑫杜瑞雪刘泽龙章群丹. 废塑料热解油烃类组成分析方法研究[J]. 石油炼制与化工, 2022, 53(5): 74-78.
[3]	朱元宝吴道洪高金森闫琛洋. 含油污泥热解及热解油加氢精制研究[J]. 石油炼制与化工, 2017, 48(1): 43-46.
[4]	陈宜俍商建超朱阳阳韩丽. 不同硅源和铝源对L沸石合成的影响[J]. 石油炼制与化工, 2013, 44(5): 10-13.